FBP-TS-SK071 Anti-Riot Shield
This shield is made of double-layer PC board, with metal edging around, effectively preventing attacks from knives, sticks, and blocking corrosive liquids. It is the preferred protective gear for law enforcement officers when carrying out tasks. The ergonomically designed handlThis shield is made of double-layer PC board, with metal edging around, effectively preventing attacks from knives, sticks, and blocking corrosive liquids. It is the preferred protective gear for law enforcement officers when carrying out tasks. The ergonomically designed handle and arm strap make it comfortable and powerful to hold. Lightweight, it can effectively reduce the burden on the holder and improve combat capability. The large protective area can effectively ensure the safety of the person behind the shield.e and arm strap make it comfortable and powerful to hold. Lightweight, it can effectively reduce the burden on the holder and improve combat capability. The large protective area can effectively ensure the safety of the person behind the shield.
FBP-TS-SK071
Quantity:
1. Appearance: The surface of the riot shield is smooth with no visible defects such as dents, bubbles, burrs, sharp angles, scratches, spots, peeling paint, or flaking. The handle of the riot shield has no burrs or sharp angles, making it easy to grip and comfortable to hold. The exposed metal parts on the shield have been surface treated and show no signs of rust.
2. Material: Made from high-quality PC material with metal edging around the shield for enhanced protection.
2. Material: Made from high-quality PC material with metal edging around the shield for enhanced protection.
3. Shield thickness: ≥3.0mm.
4. Shield dimensions: 575mm in diameter ±2mm.
5. Light transmission rate: ≥77.6%.
6. Weight: ≤2.3kg.
7. Connection strength: Components connecting the handle and those connecting the handle to the shield can withstand a pull force greater than or equal to 500 N. After testing, there was no signs of falling off, loosening, unclasping, or breaking.
8. Impact resistance strength: The shield can endure a 147J kinetic energy impact. After the impact, no puncture or crack beyond a radius of 50mm from the force point was detected.
9. Puncture resistance: The shield can withstand a puncture force of 147J of kinetic energy. After the puncture, no hole larger than 6mm or crack beyond a radius of 20mm from the force point was seen.
10. Strike resistance strength: The shield can withstand a hit at a speed of 18m/s±0.3m/s and an energy of 342J±13J without shattering or forming a crack longer than 50mm.
11. Knife resistance: The shield's upper edge can withstand a hit at a speed of 8.5m/s ± 0.5m/s and an energy level of 100J±5J. After the test, the depth of the knife mark was less than or equal to 50mm.
12. Flame retardant property: ≤10s.
13. Temperature adaptability:
① After being treated at a high temperature (+55℃±2℃, 4h), the shield was tested for striking resistance within 5 minutes. The test results meet the requirements for strike resistance.
② After being treated at a low temperature (-30℃±2℃, 4h), the shield was tested for striking resistance within 5 minutes. The test results meet the requirements for strike resistance.
② After being treated at a low temperature (-30℃±2℃, 4h), the shield was tested for striking resistance within 5 minutes. The test results meet the requirements for strike resistance.